Austenitic stainless steel has good corrosion resistance because of its high chromium content and dense oxide film. When Cr18% and Ni8% are contained, a single austenite structure can be obtained. Therefore, austenitic stainless steel has good corrosion resistance, plasticity, high temperature performance and welding performance. However, under different working conditions, austenitic stainless steel welding joints often face some special problems, which are easy to cause construction defects such as intergranular corrosion, stress corrosion, knife corrosion, welding hot cracks, α phase embrittlement and so on.

Corrosion analysis of welded joints

Intergranular corrosion of welded joints

Intergranular corrosion is one of the most important corrosion problems of austenitic stainless steel. Once intergranular corrosion occurs, its strength will almost lose when it is serious, and intergranular fracture will occur when a certain stress is applied. The intergranular corrosion of austenitic stainless steel welding joint is mainly caused by chromium carbide precipitation. When the austenitic stainless steel is sensitized in the temperature range of 500 ~ 800 ℃, the diffusion rate of supersaturated solid solution carbon to the intergranular boundary is faster than that of chromium, and the carbon in supersaturated solid solution is combined with chromium near the grain boundary, When the chromium content in the region is reduced to below the limit content (w (CR) 12.5%) required for passivation, the corrosion of the region will be accelerated and intergranular corrosion will be formed. The results show that the intergranular corrosion in the sensitized temperature zone of HAZ occurs in the region where the peak heating temperature is between 600 ℃ and 1000 ℃. The reason for intergranular corrosion is still the precipitation of chromium carbide at austenite grain boundary. The main preventive measures to reduce and prevent intergranular corrosion include:

① Small specification (small current, high welding speed) and multi pass welding are adopted;

② The carbon content in the base metal and welding material should be reduced as much as possible, and the welding material with C content less than 0.03% should be used;

③ As a result, Cr diffuses to the grain boundary more quickly in ferrite than in austenite, which reduces the phenomenon of poor chromium in austenite grain boundary;

④ The addition of Ti, Nb and other elements with stronger affinity to carbon than chromium in steel and welding materials can form stable compounds with carbon bonding, thus avoiding chromium depletion at austenite grain boundaries.

Stress corrosion of welded joints

The stress corrosion cracking of stainless steel is the most harmful corrosion behavior. There is no deformation when cracking. The accident is often sudden and the consequences are serious. There are many factors influencing the stress corrosion cracking of stainless steel under service conditions, including the composition, structure and state of the steel, the type of medium, temperature, concentration, stress properties, size and structural characteristics.

Main Problems Encountered in Welding of 18cr Austenitic Stainless Steel 2

The main measures to reduce and prevent stress corrosion are as follows:

① Avoid strong assembly, mechanical impact and arc burn, reduce cold work deformation and stress;

② Strictly control impurities in media and environment (especially chloride, fluoride, etc.);

③ Reasonable material selection (base metal, welding material): avoid grain coarsening and hardening martensite structure;

④ The weld is well formed without any stress concentration (such as undercut);

⑤ Arrange welding sequence reasonably to reduce stress;

⑥ Anti corrosion treatment: add corrosion inhibitor to coating, lining or cathodic protection.

 

Hot crack sensitivity analysis of welded joints

The hot cracks of austenitic stainless steel are mainly crystalline cracks, which are produced during the solidification process of liquid metal of weld metal. At this time, primary crystals exist in eutectic melting point, mainly between dendrites. The main reasons are as follows:

① S, P, C and so on form low melting point eutectic with Ni (for example, the melting point of NIS + Ni is 644 ℃), which weakens the grain boundary strength;

② Austenitic stainless steel has the advantages of large distance between liquidus and solidus, long crystallization time, strong dendrite orientation and easy to produce segregation of impurity elements;

③ The thermal conductivity of steel is small, and the linear expansion coefficient is large, so it is easy to produce stress.

Main Problems Encountered in Welding of 18cr Austenitic Stainless Steel 3

Main Problems Encountered in Welding of 18cr Austenitic Stainless Steel 4 

The main measures to prevent welding hot cracks include:

① The contents of harmful impurities sulfur and phosphorus in base metal and welding material shall be strictly controlled;

② About 5% ferrite is produced in the weld, which disturbs the direction of austenite columnar crystal;

③ Small current and fast welding process are adopted.

Control of ferrite content in welded joints

The content of ferrite in weld metal of austenitic steel is not only related to the formation and thermal strength of α (σ) phase embrittlement, but also directly affects the hot cracking resistance of joint. The longer the heating time, the longer the high temperature residence time, the more precipitation, which will seriously affect the mechanical properties of the joint. From the point of view of hot cracking resistance, a certain amount of ferrite is required in the weld metal. However, considering the α phase embrittlement and thermal strength, the lower the ferrite content is, the better. Therefore, the content of ferrite must be strictly controlled for high temperature strength welded joints. In some cases, austenitic weld metal must be used.

Main Problems Encountered in Welding of 18cr Austenitic Stainless Steel 5

日韩精品一区二区三区粉嫩av-欧美亚洲国产中文字幕| 亚洲国产精品一区二区av-日本一级黄色一区二区| 午夜福利卫生纸福利院-一区二区三区久久亚洲| 中文不卡一区二区三区-老司机在线老司机在线一区| 中文字幕日韩精品不卡在线一区-国产tv日韩在线观看视频| 黄色美女网站大全中文字幕-欧美韩国日本一区二区| 欧美日本亚一级二级三区久久精品-日韩欧美一区二区久久婷婷| 久久99热这里都是精品啊-国产成人亚洲精品无码aV| 亚洲国产精品一区二区av-日本一级黄色一区二区| 国产精品电影在线一区-亚洲国产大片一区二区官网| 丝袜美腿人妻连续中出-在线观看日韩三级视频| 人妻日韩精品中文字幕图片-麻豆极度性感诱人在线露脸| 亚洲国产中文欧美一区二区三区-国产精品一区二区视频成人| 中文不卡一区二区三区-老司机在线老司机在线一区| 四虎成人在线免费视频-亚洲熟女中文字幕天堂| 欧美精品一区二区三区爽爽爽-日韩国产精品亚洲经典| 国内精产熟女自线一二三区-六月丁香婷婷在线观看| 国产精品v欧美精品v日韩精品-国产欧美日韩精品区一区二污污污| 欧美一级一线在线观看-亚洲一区二区亚洲三区| 日本欧美在线视频观看-国产一区二区三区无码下载快播| 精彩亚洲一区二区三区-中文字幕中文字幕在线色站| 亚洲黑人欧美一区二区三区-亚洲一区二区三区免费视频播放| 黄色av网站在线免费观看-亚洲欧美精品偷拍tv| 国产欧美一区二区三区嗯嗯-欧美一区二区日本国产激情| 白嫩美女娇喘呻吟高潮-久久一区二区三区日产精品| 国产精品熟女视频一区二区-国产日韩精品欧美一区喷水| 熟妇勾子乱一区二区三区-欧美爱爱视频一区二区| 国产美女网站在线观看-国产精品亚洲综合网69| 丝袜高跟熟女视频国产-熟女少妇亚洲一区二区| 青青草原免费国产在线视频-精品人妻乱码一区二区三区四区| 国产精品成人欧美激情-黄色床上完整版高清无遮挡| 国产一区二区三区噜噜-精品久久亚洲一区二区欧美| 日本韩国亚洲欧美三级-日本东京不卡网一区二区三区| 国产在线观看高清精品-四季av一区二区三区中文字幕| 91大神国内精品免费网站-亚洲免费电影一区二区| 男女做爰猛烈啪啪吃奶在线观看-人妻连裤丝袜中文字幕| 国产欧美成人精品第一区-日本黄色精品一区二区| 国产欧美日本一区二区-一区二区三区亚洲在线播放| 欧美看片一区二区三区-人妻无卡精品视频在线| 亚洲国产视频不卡一区-激情欧美视频一区二区| 免费午夜福利在线观看-黄色日本黄色日本韩国黄色|