There are many causes of deformation in aluminum part machining, which are related to material properties, part geometry, and production conditions. The main factors include: deformation caused by residual stress in the blank, deformation induced by cutting forces and cutting heat, and deformation due to clamping forces.

Process Measures to Reduce Machining Deformation

Reducing Residual Stress in Blanks

Natural or artificial aging, as well as vibration treatment, can partially eliminate residual stresses in blanks. Pre-machining is also an effective method. For bulky blanks with excessive stock allowance, post-machining deformation tends to be significant. By pre-machining to remove excess material and balance stock allowance, subsequent machining deformation can be reduced. Additionally, allowing the pre-machined blank to rest helps release residual stresses.

Causes Analysis and Process Control Measures for Machining Deformation of Aluminum Components 2

Improving Tool Cutting Performance

Tool material and geometric parameters significantly influence cutting forces and heat generation. Proper tool selection is crucial for minimizing part deformation.

Optimizing Tool Geometry

Rake Angle:

A larger rake angle (while maintaining edge strength) enhances cutting sharpness, reduces chip deformation, improves chip evacuation, and lowers cutting forces and temperatures. Negative rake angles should be avoided.

Clearance Angle:

The clearance angle directly affects flank wear and surface finish. For rough milling with heavy loads and high heat, a smaller clearance angle improves heat dissipation. For finish milling, a larger clearance angle reduces friction and elastic deformation.

Helix Angle:

A higher helix angle ensures smoother milling and reduces cutting resistance.

Lead Angle:

A smaller lead angle improves heat dissipation and lowers average cutting zone temperatures.

 

Enhancing Tool Structure

Reducing Teeth Count & Increasing Chip Space:

Aluminum’s high plasticity demands larger chip pockets. Tools with fewer teeth and wider gullets are preferred.

Precision Edge Honing:

The cutting edge roughness should be below Ra = 0.4 μm. Lightly honing new tools with a fine stone removes burrs and micro-serrations, reducing heat and deformation.

Strict Wear Control:

Tool wear increases surface roughness, cutting temperature, and part deformation. Wear limits should not exceed 0.2 mm to prevent built-up edge. Workpiece temperature should stay below 100°C to avoid distortion.

machining deformation

Optimizing Workpiece Fixturing

For thin-walled aluminum parts with low rigidity:

Axial Clamping for Bushings

Radial clamping (e.g., 3-jaw chucks) causes post-machining deformation. Instead, use a threaded mandrel inserted into the part’s bore, secured axially with a endplate and nut to maintain precision during OD machining.

Vacuum Chucks for Thin Plates

Uniform clamping force distribution paired with light cuts minimizes distortion.

Filling Method

Fill hollow parts with a low-melting filler (e.g., urea-potassium nitrate melt) to enhance rigidity during machining. Dissolve the filler post-process in water/alcohol.

Strategic Process Sequencing

High-speed machining with large stock or interrupted cuts may induce vibration. A typical CNC process flow:

Roughing → Semi-finishing → Corner Cleaning → Finishing

For high-precision parts, repeat semi-finishing before final passes. Post-roughing natural cooling relieves stresses. Leave 1–2 mm stock after roughing; maintain 0.2–0.5 mm uniform allowance in finishing to ensure stability, reduce deformation, and achieve high surface quality.

Operational Techniques to Minimize Machining Deformation

In addition to the aforementioned causes, operational methods play a crucial role in controlling deformation during aluminum part machining.

Causes Analysis and Process Control Measures for Machining Deformation of Aluminum Components 3

Symmetrical Machining for Large Stock Parts

For better heat dissipation, use alternating symmetrical machining. Example: A 90mm plate machined to 60mm achieves 0.3mm flatness when processed in alternating passes versus 5mm with consecutive machining.

Layered Machining for Multi-cavity Parts

Machine all cavities layer-by-layer simultaneously to ensure uniform stress distribution, preventing deformation from uneven forces.

Optimized Cutting Parameters

Adjust depth of cut (ap) with corresponding feed rate and spindle speed increases in CNC high-speed milling to balance productivity and reduced cutting forces.

Strategic Tool Path Selection

Use conventional milling for roughing (maximum removal rate) and climb milling for finishing (better surface quality with progressive chip thickness reduction).

Thin-wall Fixturing Technique

Before final passes, briefly release and reapply minimal clamping force to allow natural recovery, applying force along the part’s most rigid direction.

Cavity Machining Method

Avoid direct plunging; pre-drill or use helical entry paths to prevent chip packing and tool breakage.

Causes Analysis and Process Control Measures for Machining Deformation of Aluminum Components 4

Conclus?o

Aluminum part deformation stems from material properties, geometry, and processing conditions, primarily involving?blank residual stresses,cutting forces/heat,and clamping stresses.The integrated application of these process optimizations and operational techniques significantly reduces deformation, enhances precision and surface quality, providing reliable technical support for production.

Deixe uma resposta

O seu endere?o de e-mail n?o será publicado. Campos obrigatórios s?o marcados com *

777米奇在线视频无码| 大鸡巴插入骚穴在线观看| 蜜臀av一区二区三区免费观| 国产精品自在拍首页| 日韩av一区二区三区激情在线| 淫荡淫水逼操烂视频| 国产熟女露脸普通话对白| 差鸡巴没码在线观看| 日韩免费一级a毛片在线播放一级| 成人黄色精品久久app| 精品麻豆亚洲欧美| 几把日逼嗯嗯视频| 新视觉亚洲三区二区一区理伦| 日韩 中文字幕在线最新| 日韩乱码一区二区三区中文字幕| 国产精品久久一区二区三区动| 中文字幕乱码一区三区免费| 99草草视频在线精品| 五月天亚洲激情综合av| 美女亚洲福利视频| 国产精品熟女视频播放| 久久久久久亚洲精品首页| 日日狠狠久久888av| 黑人巨茎和中国美女视频| 久久久久久久久黄片观看| 国产无码久久久久久| 黑人猛操日本美女| 免费国产香蕉视频在线观看| 亚洲av伦理一区二区三区久久| 91久国产在线观看| 一区二区三区av精品| 狂插美女大屁股在线观看| 精品免费久久久久久久久| 日本免费暖暖在线小视频| 国产激情内射免费精品| 久久噜噜噜久久熟女精品| 呦交小u女国产精品99| 人妻夜夜添夜夜无码AV| 无码人妻丰满熟妇区精品| 麻豆91精品96久久久| 精品少妇一区二区三区中文字幕|