Austenitic stainless steel has good corrosion resistance because of its high chromium content and dense oxide film. When Cr18% and Ni8% are contained, a single austenite structure can be obtained. Therefore, austenitic stainless steel has good corrosion resistance, plasticity, high temperature performance and welding performance. However, under different working conditions, austenitic stainless steel welding joints often face some special problems, which are easy to cause construction defects such as intergranular corrosion, stress corrosion, knife corrosion, welding hot cracks, α phase embrittlement and so on.

Corrosion analysis of welded joints

Intergranular corrosion of welded joints

Intergranular corrosion is one of the most important corrosion problems of austenitic stainless steel. Once intergranular corrosion occurs, its strength will almost lose when it is serious, and intergranular fracture will occur when a certain stress is applied. The intergranular corrosion of austenitic stainless steel welding joint is mainly caused by chromium carbide precipitation. When the austenitic stainless steel is sensitized in the temperature range of 500 ~ 800 ℃, the diffusion rate of supersaturated solid solution carbon to the intergranular boundary is faster than that of chromium, and the carbon in supersaturated solid solution is combined with chromium near the grain boundary, When the chromium content in the region is reduced to below the limit content (w (CR) 12.5%) required for passivation, the corrosion of the region will be accelerated and intergranular corrosion will be formed. The results show that the intergranular corrosion in the sensitized temperature zone of HAZ occurs in the region where the peak heating temperature is between 600 ℃ and 1000 ℃. The reason for intergranular corrosion is still the precipitation of chromium carbide at austenite grain boundary. The main preventive measures to reduce and prevent intergranular corrosion include:

① Small specification (small current, high welding speed) and multi pass welding are adopted;

② The carbon content in the base metal and welding material should be reduced as much as possible, and the welding material with C content less than 0.03% should be used;

③ As a result, Cr diffuses to the grain boundary more quickly in ferrite than in austenite, which reduces the phenomenon of poor chromium in austenite grain boundary;

④ The addition of Ti, Nb and other elements with stronger affinity to carbon than chromium in steel and welding materials can form stable compounds with carbon bonding, thus avoiding chromium depletion at austenite grain boundaries.

Stress corrosion of welded joints

The stress corrosion cracking of stainless steel is the most harmful corrosion behavior. There is no deformation when cracking. The accident is often sudden and the consequences are serious. There are many factors influencing the stress corrosion cracking of stainless steel under service conditions, including the composition, structure and state of the steel, the type of medium, temperature, concentration, stress properties, size and structural characteristics.

Main Problems Encountered in Welding of 18cr Austenitic Stainless Steel 2

The main measures to reduce and prevent stress corrosion are as follows:

① Avoid strong assembly, mechanical impact and arc burn, reduce cold work deformation and stress;

② Strictly control impurities in media and environment (especially chloride, fluoride, etc.);

③ Reasonable material selection (base metal, welding material): avoid grain coarsening and hardening martensite structure;

④ The weld is well formed without any stress concentration (such as undercut);

⑤ Arrange welding sequence reasonably to reduce stress;

⑥ Anti corrosion treatment: add corrosion inhibitor to coating, lining or cathodic protection.

 

Hot crack sensitivity analysis of welded joints

The hot cracks of austenitic stainless steel are mainly crystalline cracks, which are produced during the solidification process of liquid metal of weld metal. At this time, primary crystals exist in eutectic melting point, mainly between dendrites. The main reasons are as follows:

① S, P, C and so on form low melting point eutectic with Ni (for example, the melting point of NIS + Ni is 644 ℃), which weakens the grain boundary strength;

② Austenitic stainless steel has the advantages of large distance between liquidus and solidus, long crystallization time, strong dendrite orientation and easy to produce segregation of impurity elements;

③ The thermal conductivity of steel is small, and the linear expansion coefficient is large, so it is easy to produce stress.

Main Problems Encountered in Welding of 18cr Austenitic Stainless Steel 3

Main Problems Encountered in Welding of 18cr Austenitic Stainless Steel 4 

The main measures to prevent welding hot cracks include:

① The contents of harmful impurities sulfur and phosphorus in base metal and welding material shall be strictly controlled;

② About 5% ferrite is produced in the weld, which disturbs the direction of austenite columnar crystal;

③ Small current and fast welding process are adopted.

Control of ferrite content in welded joints

The content of ferrite in weld metal of austenitic steel is not only related to the formation and thermal strength of α (σ) phase embrittlement, but also directly affects the hot cracking resistance of joint. The longer the heating time, the longer the high temperature residence time, the more precipitation, which will seriously affect the mechanical properties of the joint. From the point of view of hot cracking resistance, a certain amount of ferrite is required in the weld metal. However, considering the α phase embrittlement and thermal strength, the lower the ferrite content is, the better. Therefore, the content of ferrite must be strictly controlled for high temperature strength welded joints. In some cases, austenitic weld metal must be used.

Main Problems Encountered in Welding of 18cr Austenitic Stainless Steel 5

hd在线观看一区二区-免费一区二区三区毛片在线| 久色高清精品在线国产-国产精品视频一区三区四区| 黑丝av少妇精品久久久久久久-中文字幕久久久人妻无码| 中文字幕日本在线资源-国产+成+人+亚洲欧洲自线| 婷婷亚洲欧美综合丁香亚洲-超刺激国语对白在线视频| 国产精品电影在线一区-亚洲国产大片一区二区官网| 久久免费观看归女高潮特黄-黄色av一本二本在线观看| 美女把腿张开给帅哥桶-无码无套少妇18p在线直播| 亚洲区欧美区在线视频-亚洲碰碰人人AV熟女天堂| 91大神国内精品免费网站-亚洲免费电影一区二区| 午夜精品午夜福利在线-内射无套内射国产精品视频| 小12萝自慰喷水亚洲网站-chinese偷拍一区二区三区| 国产精品一区二区在线免费-久久精品国产亚洲av热明星| 国产人妻人伦精品日本-国产98超碰人人做人人爱| 国产在线不卡高清一区-日本一区二区三区四区无卡| 性激烈欧美三级在线播放-久久中文字幕人妻少妇| 国产成人精品免费视频大全办公室-亚洲欧美日本综合在线| 久久亚州天堂一区二区-色噜噜色哟哟一区二区三区| 亚洲欧美精品在线一区-99热国产在线手机精品99| 国产黄污网站在线观看-成人av电影中文字幕| 国产在线不卡高清一区-日本一区二区三区四区无卡| 午夜日韩精品在线视频-亚洲网老鸭窝男人的天堂| 欧美日本亚一级二级三区久久精品-日韩欧美一区二区久久婷婷| 国产在线不卡高清一区-日本一区二区三区四区无卡| 丝袜美腿人妻连续中出-在线观看日韩三级视频| 日韩精品人妻系列一区-亚洲女同性一区二区三区| 日韩高清在线观看一区二区-美产av在线免费观看| 日本高清二区视频久二区-大香蕉在线视频大香蕉在线视频| 久久影视av一区二区-人妻激情乱偷一区二区三区| 性激烈欧美三级在线播放-久久中文字幕人妻少妇| 亚洲欧洲一区二区福利-亚洲欧美日韩高清中文| 深夜三级福利在线播放-日韩精品一区二区在线天天狠天| 四虎成人在线免费视频-亚洲熟女中文字幕天堂| 午夜福利1区2区3区-午夜洗澡免费视频网站| 亚洲国产精品日韩欧美-国产又粗又硬又大爽黄| 亚洲国产欧美日韩不卡-熟妇激情一区二区三区| 国模自慰一区二区三区-日韩一级黄色片天天看| 狠狠狠狠爱精品一二三四区-l舌熟女av国产精品| 乱入一二三免费在线观看-久久精品亚洲精品国产色婷婷| 国产美女网站在线观看-国产精品亚洲综合网69| 亚洲午夜久久久精品影院-性感美女在线观看网站国产|