Austenitic stainless steel has good corrosion resistance because of its high chromium content and dense oxide film. When Cr18% and Ni8% are contained, a single austenite structure can be obtained. Therefore, austenitic stainless steel has good corrosion resistance, plasticity, high temperature performance and welding performance. However, under different working conditions, austenitic stainless steel welding joints often face some special problems, which are easy to cause construction defects such as intergranular corrosion, stress corrosion, knife corrosion, welding hot cracks, α phase embrittlement and so on.

Corrosion analysis of welded joints

Intergranular corrosion of welded joints

Intergranular corrosion is one of the most important corrosion problems of austenitic stainless steel. Once intergranular corrosion occurs, its strength will almost lose when it is serious, and intergranular fracture will occur when a certain stress is applied. The intergranular corrosion of austenitic stainless steel welding joint is mainly caused by chromium carbide precipitation. When the austenitic stainless steel is sensitized in the temperature range of 500 ~ 800 ℃, the diffusion rate of supersaturated solid solution carbon to the intergranular boundary is faster than that of chromium, and the carbon in supersaturated solid solution is combined with chromium near the grain boundary, When the chromium content in the region is reduced to below the limit content (w (CR) 12.5%) required for passivation, the corrosion of the region will be accelerated and intergranular corrosion will be formed. The results show that the intergranular corrosion in the sensitized temperature zone of HAZ occurs in the region where the peak heating temperature is between 600 ℃ and 1000 ℃. The reason for intergranular corrosion is still the precipitation of chromium carbide at austenite grain boundary. The main preventive measures to reduce and prevent intergranular corrosion include:

① Small specification (small current, high welding speed) and multi pass welding are adopted;

② The carbon content in the base metal and welding material should be reduced as much as possible, and the welding material with C content less than 0.03% should be used;

③ As a result, Cr diffuses to the grain boundary more quickly in ferrite than in austenite, which reduces the phenomenon of poor chromium in austenite grain boundary;

④ The addition of Ti, Nb and other elements with stronger affinity to carbon than chromium in steel and welding materials can form stable compounds with carbon bonding, thus avoiding chromium depletion at austenite grain boundaries.

Stress corrosion of welded joints

The stress corrosion cracking of stainless steel is the most harmful corrosion behavior. There is no deformation when cracking. The accident is often sudden and the consequences are serious. There are many factors influencing the stress corrosion cracking of stainless steel under service conditions, including the composition, structure and state of the steel, the type of medium, temperature, concentration, stress properties, size and structural characteristics.

Main Problems Encountered in Welding of 18cr Austenitic Stainless Steel 2

The main measures to reduce and prevent stress corrosion are as follows:

① Avoid strong assembly, mechanical impact and arc burn, reduce cold work deformation and stress;

② Strictly control impurities in media and environment (especially chloride, fluoride, etc.);

③ Reasonable material selection (base metal, welding material): avoid grain coarsening and hardening martensite structure;

④ The weld is well formed without any stress concentration (such as undercut);

⑤ Arrange welding sequence reasonably to reduce stress;

⑥ Anti corrosion treatment: add corrosion inhibitor to coating, lining or cathodic protection.

 

Hot crack sensitivity analysis of welded joints

The hot cracks of austenitic stainless steel are mainly crystalline cracks, which are produced during the solidification process of liquid metal of weld metal. At this time, primary crystals exist in eutectic melting point, mainly between dendrites. The main reasons are as follows:

① S, P, C and so on form low melting point eutectic with Ni (for example, the melting point of NIS + Ni is 644 ℃), which weakens the grain boundary strength;

② Austenitic stainless steel has the advantages of large distance between liquidus and solidus, long crystallization time, strong dendrite orientation and easy to produce segregation of impurity elements;

③ The thermal conductivity of steel is small, and the linear expansion coefficient is large, so it is easy to produce stress.

Main Problems Encountered in Welding of 18cr Austenitic Stainless Steel 3

Main Problems Encountered in Welding of 18cr Austenitic Stainless Steel 4 

The main measures to prevent welding hot cracks include:

① The contents of harmful impurities sulfur and phosphorus in base metal and welding material shall be strictly controlled;

② About 5% ferrite is produced in the weld, which disturbs the direction of austenite columnar crystal;

③ Small current and fast welding process are adopted.

Control of ferrite content in welded joints

The content of ferrite in weld metal of austenitic steel is not only related to the formation and thermal strength of α (σ) phase embrittlement, but also directly affects the hot cracking resistance of joint. The longer the heating time, the longer the high temperature residence time, the more precipitation, which will seriously affect the mechanical properties of the joint. From the point of view of hot cracking resistance, a certain amount of ferrite is required in the weld metal. However, considering the α phase embrittlement and thermal strength, the lower the ferrite content is, the better. Therefore, the content of ferrite must be strictly controlled for high temperature strength welded joints. In some cases, austenitic weld metal must be used.

Main Problems Encountered in Welding of 18cr Austenitic Stainless Steel 5

亚洲欧美激情自拍色图-国产亚洲精品sese在线播放| 人妻互换精品一区二区-夜夜爽一区二区三区视频| 国产福利视频一区二区三区-日韩人妻中文视频精品| 18禁真人在线无遮挡羞免费-中文字幕精品一区二区三区四区| av网址在线直接观看-黄色av全部在线观看| 国产在线不卡高清一区-日本一区二区三区四区无卡| 久久网站中文字幕精品-三级精品久久中文字幕| 国产美女裸露无遮挡双奶网站-国产精品色午夜视频免费看| 中文字幕社区电影成人-欧美精美视频一区二区三区| 亚洲黑人欧美一区二区三区-亚洲一区二区三区免费视频播放| 天天干天天干2018-91人妻人人澡人爽精品| 亚洲另类自拍唯美另类-99国产精品兔免久久| 国产一级片久久免费看同-麻豆精品尤物一区二区青青| 91九色蝌蚪丝袜人妻-国产精品9999网站| 一区二区三区国产高清mm-美女张开腿让帅哥桶爽| 乱入一二三免费在线观看-久久精品亚洲精品国产色婷婷| 欧美成人精品巨臀大屁股-亚洲综合欧美日韩一区| 国产传媒中文字幕在线观看-午夜福利视频在线播放观看| 国产精品久久99精品毛片-国产四季高清一区二区三区| 久久影视av一区二区-人妻激情乱偷一区二区三区| 国产午夜精品理论片A级漫画-久久精品国产99亚洲精品| 国产成人高清精品免费5388-好妞色妞在线视频播放| 亚洲精品在线观看一二三区-在线观看国产中文字幕视频| 中文不卡一区二区三区-老司机在线老司机在线一区| 久久夜色精品亚洲噜国产av-大香蕉伊人猫咪在线观看| 天天日天天干天天综合-99久久综合狠狠综合久久| 黄色av网站在线免费观看-亚洲欧美精品偷拍tv| mm在线精品视频在线观看-欧美国产日韩在线一区二区三区| 欧美精品一区二区不卡-精品国产一区二区三区香蕉网址| 色婷婷六月婷婷一区二区-91草草国产欧美在线观看| 中文字幕社区电影成人-欧美精美视频一区二区三区| 日韩国产一区二区三区在线-精品日韩人妻少妇av| 亚洲欧美另类综合偷拍-婷婷社区综合在线观看| 人妻少妇无乱码中文字幕-人成免费视频一区二区| 欧美日韩黑人在线播放-51在线精品免费视频观看| 国语自产偷拍精品视频偷拍-国产伊人这里只有精品视频| 婷婷人妻少妇激情在线-欧美日韩人体艺术一区二区| 久久亚州天堂一区二区-色噜噜色哟哟一区二区三区| 三上悠亚免费观看在线-青青草原在线视频观看精品| 哦啊好大用力欧美视频-麻豆国产传媒片在线观看| 国产老熟女激情小视频-成人一区二区人妻不卡视频|