Tungsten carbide roll rings (WC rolls) are high-performance rolling mill components made from tungsten carbide (WC) particles bonded with cobalt (Co) or nickel (Ni) through powder metallurgy. They are widely used in high-speed wire rod mills, bar mills, and section mills due to their exceptional wear resistance, thermal stability, and strength.

They can be usefully used for finishing stands of high-speed wire rod mills (up to 120 m/s),precision 圧延 of rebars, alloy steels, and non-ferrous metals, and high-reduction passes where wear resistance is critical

Practical condition

Located in Guangdong Province, A metal production company commissioned its high-speed wire rod mill (with an annual capacity of 1.2 million tons of φ5.5~φ16mm wire rods) in December 2010 to enhance production efficiency and meet market demands.

The mill primarily consists of five key components: roughing mill, intermediate mill, pre-finishing mill, and finishing mill. The roughing mill features a single-line configuration with 5 stands (φ550×5) arranged in horizontal-horizontal-vertical-horizontal-vertical (HHVHV) pattern. The intermediate mill comprises 8 stands (φ550×2+φ450×4+φ350×2) with all-horizontal rolls. The pre-finishing mill has 8 stands (dual-line, 4 stands per line) configured as cantilever-type two-high mills (φ285×4×2) with alternating horizontal/vertical arrangement. The finishing mill contains 20 stands (dual-line, 10 stands per line) of cantilever-type two-high mills (gang-driven, φ228×5+φ170×5) in 45° top-cross configuration.

Due to humid climatic conditions, the mill encountered roll ring explosions caused by moisture-induced rusting of roll rings and taper sleeves. A technical task force was established to identify root causes and implement corrective measures to ensure stable production.

Practical Investigation and Solutions for Roll Ring Fractures in High-Speed Wire Rod Production 2

Production Process Overview

The manufacturing process flows as follows:

1.After single-pass rolling in the roughing mill, the billet undergoes head/tail cropping at #1 flying shear (with emergency scrap chopping capability), then diverges into dual lines via a distributor for intermediate rolling under micro-tension control.

2.Following intermediate 圧延, the stock passes through #2 flying shear for cropping before entering pre-finishing mill, where pneumatic vertical loopers enable twist-free, tensionless rolling for precise dimensional control.

3.Pre-finished stock undergoes water cooling and #3 flying shear cropping before entering finishing mill. Emergency shutoff shears activate to prevent further stock entry during malfunctions.

4.The 45° top-cross finishing mill employs gang-driven tungsten carbide roll rings for twist-free micro-tension rolling, achieving final dimensions at speeds up to 95m/s for φ5.5~7mm products.

carbide roll rings

Root Cause Analysis of Roll Ring Failures

The cost-optimized tungsten carbide roll rings exhibited these failure mechanisms:

Ambient humidity caused rust corrosion at roll ring/taper sleeve interfaces

Thermal fatigue from cyclic temperature variations (Fig.1) accelerated crack propagation

Insufficient cooling exacerbated thermal stresses (increased ΔT)

Improper assembly caused taper sleeve seizure

Brittle material properties increased handling damage risks

 

Technical Improvements & Process Controls

Material Selection Optimization

The YGR-series roll rings were selected for their Ni/Cr-enhanced properties:

1.Superior oxidation resistance (700-1000℃)

2.Improved acid corrosion resistance (pH≤7.2)

3.Enhanced thermal crack resistance

4.Optimal hardness-toughness balance across mill stands

 

Cooling System Enhancements

Implemented strict water management protocols:

1.Flow rates: 18-25m3/h per stand (slot-width dependent)

2.Pressure maintenance: 3-7bar at nozzles

3.Monthly water quality testing for particulate control

Dedicated pipe alignment inspections during maintenance

 

Optimum Rolling Tonnage

Established safe grinding thresholds at 0.2-0.4mm crack depth:

Stands 1-4: 1,800-2,500 tons

Stands 5-8: 1,500-2,000 tons

Stands 9-10: 600-1,000 tons

 

Precision Assembly Standards

Mandatory surface cleaning before assembly

Prohibited impact mounting methods

Individual roll storage in partitioned containers

Strict taper sleeve inspection/rejection criteria

 

結(jié)論

The comprehensive improvement program addressing material selection, cooling optimization, production control, and precision maintenance successfully resolved roll ring failures, achieving sustained operational stability. This methodology provides valuable reference for similar applications.

Key Recommendations

1.Select roll ring grades considering environmental factors

2.Maintain rigorous cooling water quality standards

3.Adhere to prescribed rolling tonnage limits

4.Implement precision handling and maintenance protocols

コメントを殘す

メールアドレスが公開(kāi)されることはありません。 が付いている欄は必須項(xiàng)目です

一级毛片完整版免费播放一区| 国产中文字幕在线一区二区三区| 国产一区曰韩二区欧美三区| 波多野结衣高潮尿喷| 日韩高清精品一区有码在线| 猛插女人小穴视频| 阴茎大头插少妇蜜穴视频| 精品国产自在久国产应用| 欲色福利网免费在线播放| 久久一区二区三区精华液介绍| 亚洲一区二区三区大胆视频| 中文字幕av一区二区三区蜜桃| 18岁以下禁看美女的胸| 日本不卡免费一区二区视频| 大黑屌爆操日本女人| 黑人大鸡巴双插美女| 亚洲高清中文字幕一区二区三区| 大香蕉中码手机在线视频| 看一下日本人插逼逼洞视频| 大肉棒操小骚穴视频| 丰满少妇被强入在线观看| 国产精品久久久69粉嫩| 日本最新免费不卡一区二区三区| 男生舔女生下面黄色视频| 中文字幕一高清免费视频| 久久久久黑人强伦姧人妻| 日本公共厕所mmm撒尿| 国产在线麻豆精品| 国产无圣光一区福利二区| 中国女人日逼免费片| 在线观看免费视频a v| 美国大骚逼啊啊啊| 看一下日本人插逼逼洞视频| 国产老妇伦国产熟女91| 欧美日韩在线成人| 最新免费高清无码片| 亚洲国产成久久成人综合一区| 加勒比五月综合久久伊人| 美女被插进去黄色| 一区二区三区中文欧美| 国产大码丝袜老熟女av|