Chip build-up is a tough issue. In order to reduce the consumption of cutters in batch production and lower the cost of cutter wear and tear during the production process, an analytical method combining theory and practice is adopted. By comprehensively analyzing the working conditions during the machining process, including machining efficiency, cooling methods, and product material, the adhesion of aluminum caused by the melting of aluminum is treated in practice to achieve cutter reuse, thereby reducing the cost of cutter consumption.

Chemical Treatment Method for Chip Build-up on Cutters during Aluminum Alloy Machining 2

Preface

With the rapid development of China’s automotive industry, the new energy vehicle industry has experienced exponential growth in recent years. Lightweight is a core topic in the new energy vehicle industry, and the core of lightweight is the transformation of traditional materials. Aluminum alloys, with their high strength and light weight, are indispensable materials for lightweight automotive manufacturing. The geometric shapes of auto parts are relatively complex, and the proportion of die-cast aluminum alloy parts in the whole vehicle is increasing, as is the demand for CNC machining of die-cast parts.

The CNC manufacturing of aluminum alloy auto parts mainly requires high efficiency, high stability of continuous production, and continuously reducing costs, which necessitates more detailed control and planning of the entire production process.

Chemical Treatment Method for Chip Build-up on Cutters during Aluminum Alloy Machining 3

Formation of Chip Build-up during Aluminum Alloy Machining

The main characteristic of aluminum in the machining process is its low melting point, which is manifested as “stickiness” in the working conditions. Due to this characteristic and insufficient cooling in actual working conditions, the heat generated by friction during the microscopic machining process cannot be released in a timely or effective manner. As a result, the aluminum melts and adheres to the cutting edge and chip flute of the cutter. When it cools, it instantly solidifies and adheres to the cutter, forming a chip build-up, leading to the scrapping of the cutter. This issue is commonly referred to in the industry as “easy to stick to the cutter.”

Cutters are a consumable in the CNC machining process and account for a significant portion of cost expenditures. The cutting edge of aluminum alloy-specific cutting tools should be sharper, and the chip flutes need special polishing treatment and an aluminum alloy-specific coating to improve the chip evacuation efficiency. The high-efficiency production in the automotive industry necessitates that cutters must increase feed rates and linear speeds, which in turn increases the heat generated during cutting, increases the risk of aluminum melting and sticking to the cutter, and leads to increased costs due to the scrapping of cutters caused by chip build-up.

With the requirements of environmental protection, the CNC machining of aluminum alloys extensively uses MQL (Minimum Quantity Lubrication) as a substitute for cutting fluids. The low melting point characteristic of aluminum, combined with the reduced cooling effect of MQL, further promotes the formation of chip build-up. Tools scrapped due to sticking account for about 409% of the total conventional scrapping of tools. Since traditional methods for dealing with chip build-up generally involve knocking or smashing, very few treated tools can be reused. Therefore, a new solution is proposed.

chip build-up

Treatment Measures

The specific treatment measures of the new solution are as follows:

Remove the cutter with existing chip build-up.

Find solid NaOH and dilute it with water, then place it in a ceramic container.

Once diluted into a NaOH solution, immerse the cutter with adhered aluminum into the solution, ensuring the aluminum-adhered parts are fully submerged, and continue for 2 hours, or prolong the immersion time based on the actual situation. A comparison of the traditional treatment method and the new solution is shown in Table 1.

 

Chemical Mechanism of Treating Chip Build-up

Taking the commonly used AIS7Mg material for automotive parts as an example, the content of Al is about 93.59%, the content of Si is 6.59%, and the content of Mg is 0.259%. Both Al and Si can react with NaOH solution. Soaking in NaOH solution can remove the main Al components remaining on the cutter. The principle is that the metal reacts with NaOH to produce bubbles (5), which eventually causes the adhered aluminum to fall off. The chemical reaction equations are as follows:

The reaction equation between Si and NaOH is:

Si + 2NaOH + H?O = Na?SiO? + 2H?↑

The reaction equation between Al and NaOH is:

2Al + 2NaOH + 6H?O = 2NaAl(OH)? + 3H?↑

Final conclusion: The aluminum is removed, and the cutting tool can be reused.

 

Experimental Verification

The above theory was tested using taps. The reason for choosing taps is that in aluminum alloy machining, taps are among the higher-value cutters and are tasked with a longer service life mission. Moreover, their geometric shape is complex, and the grooves are narrow, making it basically impossible to clear the adhered aluminum using physical methods after the sticking phenomenon occurs. Testing this type of cutter is more meaningful and representative.

Due to the high heat generated during machining and possible insufficient cooling, the aluminum is instantly melted and sticks in the grooves, indicating that the tap can no longer be used, and the thread profile is damaged.

According to the above chemical theory, the tap with adhered aluminum (chip build-up) was completely soaked in NaOH solution. After complete immersion in NaOH, the tap was visually inspected, and the chip build-up in the grooves had completely fallen off, with residual aluminum debris in the experimental vessel. The treated tap was used again to machine workpieces, and the thread profile of the workpiece was found to meet the requirements, with the thread being qualified. The tap could be reused.

 

結(jié)論

The automotive parts industry is characterized by mass production. The matching of new equipment and specially designed cutters requires a large amount of cutting verification during the initial setup. During the verification process, due to factors such as parameter matching, the breaking-in of new equipment, and the inexperience of the debugging personnel, the phenomenon of chip build-up on cutters is relatively common, leading to a straight-line rise in scrapping costs and production cycles. Additionally, issues such as changes in blank allowances and momentary cooling instability during the later stages of mass production, which lead to aluminum adhesion, have been effectively resolved after applying this method. This has greatly saved on cutter costs and processing time, increased the service life of the cutters, and significantly reduced the production costs for the enterprise.

コメントを殘す

メールアドレスが公開されることはありません。 が付いている欄は必須項目です

无码人妻免费一区二区三区| 美女呻吟翘臀后进爆白浆| 国产精品高潮久久久久a| 黄色软件大屌怒戳粉嫩小穴| 亚洲国产AV精品一区二区色欲| 免费男人和女人黄片| 熟妇女人妻丰满中文字幕| 国产女主播喷出白浆视频| 日本六十五十熟女一级黄色| 美女露胸露逼逼自慰| 国产一级a不收费| 国产熟女露脸普通话对白| 黄片观看骚货浪荡| 国产成人无码AV一区二区三区| 91偷自产一区二区三区蜜臀| 夫妻性生活在线免费视频| 亚洲国产无线码在线| 日韩视频无码日韩视频又2020| 亚洲二亚洲欧美一区vr| 亚洲国产区男人本色| 色999日韩自偷自拍美女| 日韩视频在线网页| 国产精品三级一区二区| 亚洲高清中文字幕一区二区三区| 小骚货舔小骚逼视频| 妺妺坐在我腿上下面好湿| 粗大长内射女人视频| 巨屌抽插舔阴视频| 中文字幕在线观一二三区| 自拍偷拍视频颜射| 大鸡巴抽插小骚逼视频免费| 久久久久黑人强伦姧人妻| 加勒比五月综合久久伊人| 欧美99热这里都是精品| 开心五月播五月亚洲第一| 日本a国产精品久久久久| 欧美亚洲熟妇视频在线观看| 久久精品欧美精品免费观看| 成年女人永久看片视频 | 日韩有码一区二区三区在线观看| 热精品韩国毛久久久久久|