Tungsten carbide roll rings (WC rolls) are high-performance rolling mill components made from tungsten carbide (WC) particles bonded with cobalt (Co) or nickel (Ni) through powder metallurgy. They are widely used in high-speed wire rod mills, bar mills, and section mills due to their exceptional wear resistance, thermal stability, and strength.

They can be usefully used for finishing stands of high-speed wire rod mills (up to 120 m/s),precision rotolamento of rebars, alloy steels, and non-ferrous metals, and high-reduction passes where wear resistance is critical

Practical condition

Located in Guangdong Province, A metal production company commissioned its high-speed wire rod mill (with an annual capacity of 1.2 million tons of φ5.5~φ16mm wire rods) in December 2010 to enhance production efficiency and meet market demands.

The mill primarily consists of five key components: roughing mill, intermediate mill, pre-finishing mill, and finishing mill. The roughing mill features a single-line configuration with 5 stands (φ550×5) arranged in horizontal-horizontal-vertical-horizontal-vertical (HHVHV) pattern. The intermediate mill comprises 8 stands (φ550×2+φ450×4+φ350×2) with all-horizontal rolls. The pre-finishing mill has 8 stands (dual-line, 4 stands per line) configured as cantilever-type two-high mills (φ285×4×2) with alternating horizontal/vertical arrangement. The finishing mill contains 20 stands (dual-line, 10 stands per line) of cantilever-type two-high mills (gang-driven, φ228×5+φ170×5) in 45° top-cross configuration.

Due to humid climatic conditions, the mill encountered roll ring explosions caused by moisture-induced rusting of roll rings and taper sleeves. A technical task force was established to identify root causes and implement corrective measures to ensure stable production.

Practical Investigation and Solutions for Roll Ring Fractures in High-Speed Wire Rod Production 2

Production Process Overview

The manufacturing process flows as follows:

1.After single-pass rolling in the roughing mill, the billet undergoes head/tail cropping at #1 flying shear (with emergency scrap chopping capability), then diverges into dual lines via a distributor for intermediate rolling under micro-tension control.

2.Following intermediate rotolamento, the stock passes through #2 flying shear for cropping before entering pre-finishing mill, where pneumatic vertical loopers enable twist-free, tensionless rolling for precise dimensional control.

3.Pre-finished stock undergoes water cooling and #3 flying shear cropping before entering finishing mill. Emergency shutoff shears activate to prevent further stock entry during malfunctions.

4.The 45° top-cross finishing mill employs gang-driven tungsten carbide roll rings for twist-free micro-tension rolling, achieving final dimensions at speeds up to 95m/s for φ5.5~7mm products.

carbide roll rings

Root Cause Analysis of Roll Ring Failures

The cost-optimized tungsten carbide roll rings exhibited these failure mechanisms:

Ambient humidity caused rust corrosion at roll ring/taper sleeve interfaces

Thermal fatigue from cyclic temperature variations (Fig.1) accelerated crack propagation

Insufficient cooling exacerbated thermal stresses (increased ΔT)

Improper assembly caused taper sleeve seizure

Brittle material properties increased handling damage risks

 

Technical Improvements & Process Controls

Material Selection Optimization

The YGR-series roll rings were selected for their Ni/Cr-enhanced properties:

1.Superior oxidation resistance (700-1000℃)

2.Improved acid corrosion resistance (pH≤7.2)

3.Enhanced thermal crack resistance

4.Optimal hardness-toughness balance across mill stands

 

Cooling System Enhancements

Implemented strict water management protocols:

1.Flow rates: 18-25m3/h per stand (slot-width dependent)

2.Pressure maintenance: 3-7bar at nozzles

3.Monthly water quality testing for particulate control

Dedicated pipe alignment inspections during maintenance

 

Optimum Rolling Tonnage

Established safe grinding thresholds at 0.2-0.4mm crack depth:

Stands 1-4: 1,800-2,500 tons

Stands 5-8: 1,500-2,000 tons

Stands 9-10: 600-1,000 tons

 

Precision Assembly Standards

Mandatory surface cleaning before assembly

Prohibited impact mounting methods

Individual roll storage in partitioned containers

Strict taper sleeve inspection/rejection criteria

 

Conclusione

The comprehensive improvement program addressing material selection, cooling optimization, production control, and precision maintenance successfully resolved roll ring failures, achieving sustained operational stability. This methodology provides valuable reference for similar applications.

Key Recommendations

1.Select roll ring grades considering environmental factors

2.Maintain rigorous cooling water quality standards

3.Adhere to prescribed rolling tonnage limits

4.Implement precision handling and maintenance protocols

Lascia un commento

Il tuo indirizzo email non sarà pubblicato. I campi obbligatori sono contrassegnati *

24日本精品视频免费| 免费骚逼潮吹av| 国产女主播喷出白浆视频| 最新中文字幕av不卡高清| 夜夜38亚洲综合网| 欲色福利网免费在线播放| 男人的下面进女人的下面在线观看| 黄色av成年人在线观看| 免费观看的黄视频一级国产| 国产 日韩 亚洲 一区| 国产成人亚洲欧美久久| 潮中文字幕在线观看| 使劲操我小穴视频| 伊人久久综合无码成人网| 美女被插入小穴涩涩视频| 色哟哟精品视频一区二区| 在线观看国产黄色| 亚洲男人的天堂2021| 欧美一级免费观看| 亚洲av一区二区在线看| 大屌把女生逼逼操肿国产| 玩弄邻居少妇呻吟11p| 欧美黑屌操B内射冒白浆| 欧美日韩亚洲人人夜夜澡| 欧美一区二区三区久久国产精品| 日韩久久中文字幕| 丰满少妇被强入在线观看| 我最爱操女人的骚逼| 蜜臀AV无码国产精品尤物| 亚洲国产无线码在线| 欧美 日本 亚洲 国产| 大鸡巴日大鸡巴在线观看| 日本最新免费不卡一区二区三区| 日韩素人精品亚洲热一区| 国产女主播喷出白浆视频| 伊人久久久久久久久香港| 捆绑调教白浆一区二区三区| 成人久久久久久蜜桃免费| 蜜臀AV无码国产精品尤物| 亚洲日韩国产欧美久久久| 美女穿黑丝被大鸡巴猛操|