Austenitic stainless steel has good corrosion resistance because of its high chromium content and dense oxide film. When Cr18% and Ni8% are contained, a single austenite structure can be obtained. Therefore, austenitic stainless steel has good corrosion resistance, plasticity, high temperature performance and welding performance. However, under different working conditions, austenitic stainless steel welding joints often face some special problems, which are easy to cause construction defects such as intergranular corrosion, stress corrosion, knife corrosion, welding hot cracks, α phase embrittlement and so on.

Corrosion analysis of welded joints

Intergranular corrosion of welded joints

Intergranular corrosion is one of the most important corrosion problems of austenitic stainless steel. Once intergranular corrosion occurs, its strength will almost lose when it is serious, and intergranular fracture will occur when a certain stress is applied. The intergranular corrosion of austenitic stainless steel welding joint is mainly caused by chromium carbide precipitation. When the austenitic stainless steel is sensitized in the temperature range of 500 ~ 800 ℃, the diffusion rate of supersaturated solid solution carbon to the intergranular boundary is faster than that of chromium, and the carbon in supersaturated solid solution is combined with chromium near the grain boundary, When the chromium content in the region is reduced to below the limit content (w (CR) 12.5%) required for passivation, the corrosion of the region will be accelerated and intergranular corrosion will be formed. The results show that the intergranular corrosion in the sensitized temperature zone of HAZ occurs in the region where the peak heating temperature is between 600 ℃ and 1000 ℃. The reason for intergranular corrosion is still the precipitation of chromium carbide at austenite grain boundary. The main preventive measures to reduce and prevent intergranular corrosion include:

① Small specification (small current, high welding speed) and multi pass welding are adopted;

② The carbon content in the base metal and welding material should be reduced as much as possible, and the welding material with C content less than 0.03% should be used;

③ As a result, Cr diffuses to the grain boundary more quickly in ferrite than in austenite, which reduces the phenomenon of poor chromium in austenite grain boundary;

④ The addition of Ti, Nb and other elements with stronger affinity to carbon than chromium in steel and welding materials can form stable compounds with carbon bonding, thus avoiding chromium depletion at austenite grain boundaries.

Stress corrosion of welded joints

The stress corrosion cracking of stainless steel is the most harmful corrosion behavior. There is no deformation when cracking. The accident is often sudden and the consequences are serious. There are many factors influencing the stress corrosion cracking of stainless steel under service conditions, including the composition, structure and state of the steel, the type of medium, temperature, concentration, stress properties, size and structural characteristics.

Main Problems Encountered in Welding of 18cr Austenitic Stainless Steel 2

The main measures to reduce and prevent stress corrosion are as follows:

① Avoid strong assembly, mechanical impact and arc burn, reduce cold work deformation and stress;

② Strictly control impurities in media and environment (especially chloride, fluoride, etc.);

③ Reasonable material selection (base metal, welding material): avoid grain coarsening and hardening martensite structure;

④ The weld is well formed without any stress concentration (such as undercut);

⑤ Arrange welding sequence reasonably to reduce stress;

⑥ Anti corrosion treatment: add corrosion inhibitor to coating, lining or cathodic protection.

 

Hot crack sensitivity analysis of welded joints

The hot cracks of austenitic stainless steel are mainly crystalline cracks, which are produced during the solidification process of liquid metal of weld metal. At this time, primary crystals exist in eutectic melting point, mainly between dendrites. The main reasons are as follows:

① S, P, C and so on form low melting point eutectic with Ni (for example, the melting point of NIS + Ni is 644 ℃), which weakens the grain boundary strength;

② Austenitic stainless steel has the advantages of large distance between liquidus and solidus, long crystallization time, strong dendrite orientation and easy to produce segregation of impurity elements;

③ The thermal conductivity of steel is small, and the linear expansion coefficient is large, so it is easy to produce stress.

Main Problems Encountered in Welding of 18cr Austenitic Stainless Steel 3

Main Problems Encountered in Welding of 18cr Austenitic Stainless Steel 4 

The main measures to prevent welding hot cracks include:

① The contents of harmful impurities sulfur and phosphorus in base metal and welding material shall be strictly controlled;

② About 5% ferrite is produced in the weld, which disturbs the direction of austenite columnar crystal;

③ Small current and fast welding process are adopted.

Control of ferrite content in welded joints

The content of ferrite in weld metal of austenitic steel is not only related to the formation and thermal strength of α (σ) phase embrittlement, but also directly affects the hot cracking resistance of joint. The longer the heating time, the longer the high temperature residence time, the more precipitation, which will seriously affect the mechanical properties of the joint. From the point of view of hot cracking resistance, a certain amount of ferrite is required in the weld metal. However, considering the α phase embrittlement and thermal strength, the lower the ferrite content is, the better. Therefore, the content of ferrite must be strictly controlled for high temperature strength welded joints. In some cases, austenitic weld metal must be used.

Main Problems Encountered in Welding of 18cr Austenitic Stainless Steel 5

亚洲欧美激情自拍色图-国产亚洲精品sese在线播放| 欧美一级一线在线观看-亚洲一区二区亚洲三区| 国产亚洲欧美一区91-亚洲欧美一区二区在线| 久久精品亚洲无中文东京热-日本妹子内谢视频一区| 久久人妻一区二区三区欧美-国内不卡的一区二区三区| 91九色蝌蚪丝袜人妻-国产精品9999网站| 国产人妻人伦精品日本-国产98超碰人人做人人爱| 乱入一二三免费在线观看-久久精品亚洲精品国产色婷婷| 欧美看片一区二区三区-人妻无卡精品视频在线| 99在线免费观看视频-丰满人妻一区二区三区视频53| 国产成人精品免费视频大全办公室-亚洲欧美日本综合在线| 丝袜美腿人妻连续中出-在线观看日韩三级视频| 18禁真人在线无遮挡羞免费-中文字幕精品一区二区三区四区| 久久精品人妻一区二区三区极品-久久99热这里只有精品免费| 91大神国内精品免费网站-亚洲免费电影一区二区| 国语自产偷拍精品视频偷拍-国产伊人这里只有精品视频| 亚洲永久免费在线观看-亚洲欧美导航一区二区导航| 亚洲av日韩五月天久热精品-国产日韩欧美一区二区三区群战| 亚洲精品激情一区二区-久久成人国产欧美精品一区二区| 乱入一二三免费在线观看-久久精品亚洲精品国产色婷婷| 亚洲区欧美区在线视频-亚洲碰碰人人AV熟女天堂| 黄片一区二区三区在线看-偷拍一区二区在线观看| 91大神国内精品免费网站-亚洲免费电影一区二区| 一区二区国产高清在线-日本高清无卡一区二区三区| 亚洲精品激情一区二区-久久成人国产欧美精品一区二区| 91精品国产无线乱码在线-999精品视频免费看| 亚洲欧美精品在线一区-99热国产在线手机精品99| 国产欧美一区二区三区嗯嗯-欧美一区二区日本国产激情| 日本中文字幕啊啊啊啊-久久精品伊人久久精品伊人| 日韩精品人妻系列一区-亚洲女同性一区二区三区| 九九热这里只有精品九九-欧美日韩人妻精品一二三| 99久热精品免费观看四虎-亚洲天堂精品视频在线| 18禁真人在线无遮挡羞免费-中文字幕精品一区二区三区四区| 久久精品国产96精品-日韩人成理论午夜福利| 看肥婆女人黄色儿逼视频-秋霞电影一区二区三区四区| 欧美精品国产白浆久久正在-国产精彩视频一区二区三区| 国产精品成人欧美激情-黄色床上完整版高清无遮挡| 亚洲av乱码一区二区-九九免费在线观看视频| 亚洲黄片三级三级三级-国产成人一区二区在线视频| 色婷婷六月婷婷一区二区-91草草国产欧美在线观看| 婷婷亚洲欧美综合丁香亚洲-超刺激国语对白在线视频|