There are many causes of deformation in aluminum part machining, which are related to material properties, part geometry, and production conditions. The main factors include: deformation caused by residual stress in the blank, deformation induced by cutting forces and cutting heat, and deformation due to clamping forces.

Process Measures to Reduce Machining Deformation

Reducing Residual Stress in Blanks

Natural or artificial aging, as well as vibration treatment, can partially eliminate residual stresses in blanks. Pre-machining is also an effective method. For bulky blanks with excessive stock allowance, post-machining deformation tends to be significant. By pre-machining to remove excess material and balance stock allowance, subsequent machining deformation can be reduced. Additionally, allowing the pre-machined blank to rest helps release residual stresses.

Causes Analysis and Process Control Measures for Machining Deformation of Aluminum Components 2

Improving Tool Cutting Performance

Tool material and geometric parameters significantly influence cutting forces and heat generation. Proper tool selection is crucial for minimizing part deformation.

Optimizing Tool Geometry

Rake Angle:

A larger rake angle (while maintaining edge strength) enhances cutting sharpness, reduces chip deformation, improves chip evacuation, and lowers cutting forces and temperatures. Negative rake angles should be avoided.

Clearance Angle:

The clearance angle directly affects flank wear and surface finish. For rough milling with heavy loads and high heat, a smaller clearance angle improves heat dissipation. For finish milling, a larger clearance angle reduces friction and elastic deformation.

Helix Angle:

A higher helix angle ensures smoother milling and reduces cutting resistance.

Lead Angle:

A smaller lead angle improves heat dissipation and lowers average cutting zone temperatures.

 

Enhancing Tool Structure

Reducing Teeth Count & Increasing Chip Space:

Aluminum’s high plasticity demands larger chip pockets. Tools with fewer teeth and wider gullets are preferred.

Precision Edge Honing:

The cutting edge roughness should be below Ra = 0.4 μm. Lightly honing new tools with a fine stone removes burrs and micro-serrations, reducing heat and deformation.

Strict Wear Control:

Tool wear increases surface roughness, cutting temperature, and part deformation. Wear limits should not exceed 0.2 mm to prevent built-up edge. Workpiece temperature should stay below 100°C to avoid distortion.

machining deformation

Optimizing Workpiece Fixturing

For thin-walled aluminum parts with low rigidity:

Axial Clamping for Bushings

Radial clamping (e.g., 3-jaw chucks) causes post-machining deformation. Instead, use a threaded mandrel inserted into the part’s bore, secured axially with a endplate and nut to maintain precision during OD machining.

Vacuum Chucks for Thin Plates

Uniform clamping force distribution paired with light cuts minimizes distortion.

Filling Method

Fill hollow parts with a low-melting filler (e.g., urea-potassium nitrate melt) to enhance rigidity during machining. Dissolve the filler post-process in water/alcohol.

Strategic Process Sequencing

High-speed machining with large stock or interrupted cuts may induce vibration. A typical CNC process flow:

Roughing → Semi-finishing → Corner Cleaning → Finishing

For high-precision parts, repeat semi-finishing before final passes. Post-roughing natural cooling relieves stresses. Leave 1–2 mm stock after roughing; maintain 0.2–0.5 mm uniform allowance in finishing to ensure stability, reduce deformation, and achieve high surface quality.

Operational Techniques to Minimize Machining Deformation

In addition to the aforementioned causes, operational methods play a crucial role in controlling deformation during aluminum part machining.

Causes Analysis and Process Control Measures for Machining Deformation of Aluminum Components 3

Symmetrical Machining for Large Stock Parts

For better heat dissipation, use alternating symmetrical machining. Example: A 90mm plate machined to 60mm achieves 0.3mm flatness when processed in alternating passes versus 5mm with consecutive machining.

Layered Machining for Multi-cavity Parts

Machine all cavities layer-by-layer simultaneously to ensure uniform stress distribution, preventing deformation from uneven forces.

Optimized Cutting Parameters

Adjust depth of cut (ap) with corresponding feed rate and spindle speed increases in CNC high-speed milling to balance productivity and reduced cutting forces.

Strategic Tool Path Selection

Use conventional milling for roughing (maximum removal rate) and climb milling for finishing (better surface quality with progressive chip thickness reduction).

Thin-wall Fixturing Technique

Before final passes, briefly release and reapply minimal clamping force to allow natural recovery, applying force along the part’s most rigid direction.

Cavity Machining Method

Avoid direct plunging; pre-drill or use helical entry paths to prevent chip packing and tool breakage.

Causes Analysis and Process Control Measures for Machining Deformation of Aluminum Components 4

Conclusión

Aluminum part deformation stems from material properties, geometry, and processing conditions, primarily involving?blank residual stresses,cutting forces/heat,and clamping stresses.The integrated application of these process optimizations and operational techniques significantly reduces deformation, enhances precision and surface quality, providing reliable technical support for production.

Deja una respuesta

Tu dirección de correo electrónico no será publicada. Los campos obligatorios están marcados con *

国产亚洲精品一区久久| 大鸡巴插我在线观看| 国产精品一区二区三区涩涩av| 美女穿黑丝被大鸡巴猛操| 欧美日韩国产这里只有精品| 美国大骚逼啊啊啊| 看看美日韩操逼吧| 国产高清第一区第二区第一页| 在线12萝自慰喷水| 黑人巨茎和中国美女视频| 三上悠亚精品一区二区久久| 老司机精品免费在线视频| 大香蕉操逼小视频| 日韩av一区二区高清不卡| 在线 中文字幕 第一页| 天美传媒精品1区2区3区| 欧美精品第15页| 精彩欧美一区二区三区| 久久久久久亚洲精品首页| 亚洲av熟妇高潮精品啪啪| 国产精品视频一区二区三区八戒| 欧美日韩在线成人| 久久精品国产亚洲高清| 亚洲v国产v天堂a无码| 久久一级高潮a免费| 久久久精品日韩一区二区三区| 久久综合久久久久综合大| 精品人妻一区二区三区日产乱码| 欧美国产日韩a欧美在线| 欧美日韩亚洲人人夜夜澡| 西瓜在线看免费观看视频| 大阴茎交于大阴户黄片视频| 操纯欲女生小穴视频| 束缚久久久久久免费高潮| 国产日女人视频在线观看| 日韩一区二区三区国色天香| 久久精品欧美精品免费观看| 国产亚洲精品高清视频免费| 国产精品538一区二区在线| 欧美大胆a级视频 一本| 鸡巴抽插逼逼视频|