Coarse Tungsten Carbide (WC) is a fundamental raw material for producing coarse WC-Co alloys. The classic method for producing this tungsten carbide involves high-temperature reduction of tungsten oxide and high-temperature carburization. The Fischer particle size of tungsten carbide ranges from about 10 μm to over 20 μm. The coarser the particles, the higher the manufacturing cost. Choosing high-quality and cost-effective raw powder is an important consideration for many alloy and tool manufacturers. This study selects tungsten carbide powders with significantly different particle sizes and investigates the relationship between the characterization parameters of these powders and the grain size of the alloy. The aim is to provide insights that could help reduce energy and material consumption in the manufacture of coarse-grained alloys.

 

Experimental Methods

Raw Materials

The experiment uses coarse and extra-coarse WC powders from well-known suppliers, with their main characteristics shown in Table 1. Additionally, 2.0 μm cobalt powder from the same supplier was also used.

particle size

Experimental Methods

For the preparation of WC-10%Co (where all content is given in weight percentage), weigh 900 g of WC, 100 g of Co, and 20 g of PEG. Measure 235 mL of alcohol and 2000 g of grinding balls. Add these into a 2.4 L ball mill. The mill is operated at a speed of 63 r/min for 14.5 hours. After milling, the mixture is dried, sieved, and then pressed into samples weighing 10 g each. The samples are sintered in a continuous vacuum sintering furnace at 1450°C.

Particle Size Measurement

For coarse tungsten carbide, measure the Fischer particle size in both the as-supplied and milled states. The samples are resin-mounted and analyzed using a metallurgical microscope to determine the grain size and particle size distribution of the powder. The alloy grain size and particle size distribution are measured using classic metallographic methods, and the coercive force of the samples is also assessed.

 

 

Results and Analysis

Fischer Particle Size (Fsss) and Alloy Grain Size

As-Supplied Particle Size and Alloy Grain Size

The metallographic images of alloys made from WC powders #1 and #2 are shown in Figures 1 and 2, respectively. Comparing Figures 1 and 2, it can be observed that the WC grain size in Figure 2 appears to be slightly coarser than in Figure 1. This indicates that coarser as-supplied Fsss particle sizes of WC lead to coarser grain sizes in the WC-Co alloys. Metallographic analysis shows that the average WC grain sizes for alloys made from powders #1 and #2 are 4.8 μm and 5.8 μm, respectively. Thus, the average grain size of WC in sample #2 is 1.2 times that in sample #1. The as-supplied Fsss particle size of #2 WC powder is 2.5 times that of #1 WC powder. Clearly, there is no direct proportional relationship between the as-supplied Fsss particle size of WC powder and the alloy grain size. Additionally, the Fsss particle size values for #1 WC powder are 2.5 times the alloy grain size, and for #2 WC powder, it is 5.3 times the alloy grain size. This indicates that the as-supplied WC powders for both samples are primarily aggregated polycrystalline WC particles, with more severe agglomeration for coarser WC powders.

?The 3 Impact of Coarse Tungsten Carbide Particle Size on WC-Co Alloy Grain Size 2

?The 3 Impact of Coarse Tungsten Carbide Particle Size on WC-Co Alloy Grain Size 3

Milled Particle Size and Alloy Grain Size

Comparing Table 1 with the metallographic grain sizes in Figures 1 and 2, it can be seen that the Fsss particle sizes of milled WC powders #1 and #2 are relatively close to the alloy grain sizes. Moreover, the measured alloy grain sizes are higher than the milled Fsss particle size values. This discrepancy is due to differences in measurement principles as well as grain growth during the sintering process. However, it clearly indicates that the Fsss particle sizes of coarse WC powders in the milled state are very close to the alloy grain sizes. The ratios of average grain sizes to milled particle sizes for alloys #1 and #2 are 1.15 and 1.31, respectively.

Raw Material WC Grain Size and Alloy Grain Size

Results from Direct Metallographic Measurement

Metallographic images of #1 and #2 WC powders after mounting and etching are shown in Figures 3 and 4. The grain sizes measured using metallographic methods are 5.31 μm and 8.5 μm, respectively. The grain size distributions of the powders and alloys are shown in Figures 5 and 6.

?The 3 Impact of Coarse Tungsten Carbide Particle Size on WC-Co Alloy Grain Size 4 ?The 3 Impact of Coarse Tungsten Carbide Particle Size on WC-Co Alloy Grain Size 5

Figures 3 and 4 clearly indicate that the grain size of #2 WC is significantly larger than that of #1 WC. This suggests that WC with a coarser as-supplied Fischer particle size also has coarser grains. Additionally, it is evident that #1 WC exhibits better dispersion, with less pronounced sintering between particles compared to #2 WC. The severe sintering in #2 WC particles is a major reason why the metallographic grain size is much larger than the alloy grain size, and also explains why the grains in #2 WC are much larger than those in #1 WC.

From the grain size distribution of the raw powders and alloys in Figures 5 and 6, it can be seen that sample #1 contains coarse WC grains of 15–20 μm in the raw material, which are not present in the alloy. In contrast, sample #2 has a substantial amount of WC grains in the 15–35 μm range, though only a small amount of 15–20 μm grains are found in the alloy. This suggests that the severe sintering of the mounted WC, although difficult to distinguish by metallographic methods after etching, was fragmented during the intense grinding process.

Moreover, comparing the WC and alloy grain size distributions in Figures 5 and 6 shows that the grain size distribution of WC in sample #1 is more consistent with the alloy grain distribution than in sample #2. This consistency is a significant reason why many researchers believe that WC similar to sample #1 is more conducive to producing coarse alloys with a more uniform grain size.

WC Particle Size and Alloy Coercive Force

The coercive forces of the alloys made from #1 and #2 powders are 4.6 kA/m and 4.3 kA/m, respectively. The relationship between the WC-Co alloy grain size and the alloy’s coercive force can be expressed using the empirical formula (1).

?The 3 Impact of Coarse Tungsten Carbide Particle Size on WC-Co Alloy Grain Size 6

In the formula:

  • Hc= coercive force of the alloy (kA/m)
  • Com= cobalt content in the alloy (%)
  • Dwc= average WC grain size in the alloy (μm)

 

According to the calculations, the average grain sizes of alloys #1 and #2 are 7.4 μm and 8.8 μm, respectively. Clearly, the calculated grain sizes are significantly larger than the measured grain sizes, but the difference between the average grain sizes of alloys #2 and #1 is close to the difference observed using metallographic methods. The results obtained from formula (1) do not show a clear quantitative relationship with the Fsss particle sizes of the raw WC in both states, but the size of the raw material particles can still be used to predict the alloy grain size and coercive force.

Conclusions

Based on the above, the following conclusions can be drawn:

1.Coarse WC powders with larger as-supplied Fsss particle sizes tend to have higher milled Fsss particle sizes and larger grain sizes, leading to alloys with larger grain sizes.

2.The Fsss particle size in the milled state of coarse WC can be used to evaluate the grain size of coarse WC and predict the grain size of WC-Co alloys. Under the test conditions, the alloy grain size is 1.1 to 1.3 times the Fsss particle size of the milled WC.

3.Coarse WC powders with as-supplied Fsss particle sizes around 10 μm have a better consistency in grain size distribution with the alloy WC grain size distribution compared to extremely coarse WC powders with Fsss particle sizes above 25 μm.

???? ???????

?? ??? ??? ????? ????? ??????????. ?????? ????????? ???? ????? ?? *

中文字幕一区二区三区中文字幕| 韩国年轻的母亲在线观看| 亚洲国产成久久成人综合一区| 美女扒开腿让男人桶爽揉| 男人大鸡巴操小鲜肉视频| 色狠狠久久av北条麻妃| 日韩美女一区二区三区香蕉视频| 99久久国产综合精品女| 另类亚洲欧美专区第一页| 99视频在线看免费视频| 99视频在线看免费视频| 大鸡巴操饿罗斯女人| 新视觉亚洲三区二区一区理伦| av人摸人人人澡人人超| 中文字幕乱码人妻一区二区三区| 乱伦美女小骚货视频| 留学生美女被大黑屌猛戳| 制服丝袜国产在线第一页| 人人超级碰青青精品| 欧美黑屌操B内射冒白浆| 麻豆91精品96久久久| 人妻少妇精品视频12p| 美女让我插她的骚逼| 女人182毛片a级毛片| 美女张开腿让男人桶91| 欧美黄色三级成人小视频| 人人摸人 人干人人草操| 欧美日韩国产这里只有精品| 东北大吊干东北少妇AV| 日本一区二区不卡在线国产| 天天免费的无码AV| 欧美十八一区二区三区| 色哟哟精品视频一区二区| 内射后入在线观看一区| 中国女人日逼免费片| 亚洲精品国产综合一线久久| 日本不卡高清视频在线播放| 91性潮久久久久久久久| 国产163黄网人看人人爽| 一区二区国产精品免费视频| 伊人成人精品在线|